Assessment of surface and electrical properties of the TiO2@zeolite hybrid materials

Jan 06, 2024

Scientific Reports volume 13, Article number: 3650 (2023) Cite this article

Degradation of pollutants in aqueous medium is of high interest due to the impact on environment and human health, therefore, design and study of the physico-chemical properties of photocatalysts for water remediation are of major significance. Among properties of photocatalyst, those related to the surface and electrical mechanism are crucial to the photocatalyst´s performance. Here we report the chemical and morphological characteristics of TiO2@zeolite photocatalyst by X-ray photoelectron spectroscopy (XPS) and scanning electron microscopy (SEM) respectively, and a coherent electrical conduction mechanism was proposed based on data obtained from assisted laser impedance spectroscopy (ALIS), in which the zeolite was synthesized from recycled coal fly ash. The results obtained by SEM and XPS verified the presence of spherical particles of TiO2 anatase with presence of Ti3+ state. ALIS results showed that impedance of the entire system increases when the amount of TiO2 increases and the samples with lower capacitive performance allowed a larger transfer of the charges between the solid–liquid interface. All results showed that higher photocatalytic performance of TiO2 growth over hydroxysodalite with 8.7 wt% and 25 wt% of TiO2 can be explained in terms of the morphology of TiO2 and the interactions between substrate-TiO2 mainly.

Among the dyes, the azo compounds are widely used in the food and textile industries, a considerable amount of the wastewater of those industries are released to the environment which represent a hazard for humans and aquatic life1,2. Due to a high chemical stability of dyes the advanced oxidation processes using heterogeneous photocatalysis allows the purification of this class of wastewater3. Amid photocatalysts, the TiO2 is one of the most used in the photodegradation of pollutants due to its properties such as high oxidation efficiency, chemical and biological inertness, high photostability, ease of production and usage in comparison with other ones, relatively low cost, and environmentally friendly4,5; thus, the TiO2 has been used and is still studied as a fundamental material in order to improve photocatalyst processes6,7,8,9,10,11,12,13. To enhance the performance of TiO2, this is grown and dispersed over an adequate substrate creating a hybrid material that uses the properties of both TiO2 and substrate. One of the used substrates to immobilize TiO2 is the zeolite, which is a hydrated aluminosilicate consisting of TO4 (T = Si, Al) tetrahedral units linked through an oxygen atom; they generate a three-dimensional structure with inner cavities and pores of molecular dimensions interconnected by channels. Due to the difference in oxidation state of the Al (+3) and the Si (+4) ions, a negative charge appears, which is neutralized by the exchangeable cations (Na+, K+, Ca2+, Mg2+) and by adsorbed water molecules that are placed in the channels or cages of the structure14,15. The zeolites are of natural or synthetic origin and are used in numerous applications such as agriculture16, health17, hydrocarbons18, and pollution treatment19. Synthetic zeolites can be synthesized from waste materials such as glass and aluminum scraps20, coal fly ash (CFA)21, lithium waste22, and rice husk23, among others, by hydrothermal method, mainly. The photocatalyst's ability to degrade pollutants by TiO2@zeolite materials is due to the property of the electron–hole pair, promoted by the adsorption of light by TiO2 to produce free radicals in an aqueous medium, radicals capable of oxidizing organic compounds as azo dyes4,5. The photocatalysis efficiency of the TiO2 depends on the number of free radicals produced, which is influenced by the adsorption capability and the recombination of the electron–hole, mainly. The dispersion of TiO2 in a zeolite searches to solve any difficulties of the TiO2—such as the reduction of the recombination electron–hole rate—, increases the adsorption, and facilitates the recuperation from a liquid solution24. According to the literature review, the production of hybrid materials of TiO2@zeolite has been reported with commercial zeolite mostly25,26,27,28; however, the literature related to the use of zeolite synthesized from coal fly ash to the production of TiO2@zeolite are scarce24,29, consequently a lack of the understanding of the mechanism involved for photocatalysis applications in those materials still.

In a previous work30, we reported the synthesis of low cost TiO2@zeolite using CFA treated by hydrothermal method. A variation of the experimental parameters allowed to obtain two samples with hydroxysodalite and cancrinite zeolite as a majoritarian phase, these samples were labeled as HYD and CAN respectively. By the impregnation method, different nominal amounts of TiO2 (wt%) in the form of titanium isopropoxide were deposited and dispersed on the surface of the HYD and the CAN separately. The structural phase of the TiO2 was confirmed to be anatase by employing X-ray diffraction, Raman measurements, and high-resolution transmission electron microscopy. Ti3+ state, due to oxygen vacancies in the TiO2 structure, was confirmed by electron spin resonance measurements. Photocatalytic degradation of an azo dye was tested with methyl orange under UV radiation; samples with lower amount of TiO2 (8.7 wt% and 25 wt%) deposited on HYD showed the higher degradation performance.

In this work we report the study of surface and electrical characteristics of previously synthesized TiO2@zeolite hybrid materials; these materials, obtained with concentration different of TiO2, were characterized employing SEM, XPS, and photoimpedance measurements. The study aimed to correlate the structural, morphological, and electrical properties to propose a coherent mechanism about charge transfer that explain the photocatalytic degradation of methyl orange previously reported by this kind of materials.

The synthesis of TiO2@zeolite is described in ref30 briefly. CFA was collected at Sochagota TermoPaipa IV station power plant (Boyacá, Colombia) and passed through 400 sieve mesh (38 μm) with a main chemical composition of Si and Al oxides and Si/Al ratio of 2.4. The CFA was activated by the conventional hydrothermal method. Hydroxysodalite (HYD) zeolite as a majoritarian phase was obtained using 4.2 g of CFA mixed into a distilled water solution of NaOH with a NaOH/CFA ratio of 3.0 at 99.5 °C for 24 h and post-heat treatment at 500 °C. Cancrinite (CAN) zeolite as a majoritarian phase was synthesized using 10 g of CFA mixed into a distilled water solution of NaOH with a NaOH/CFA ratio of 1.7 at 95 °C for 24 h and post-heat treatment at 500 °C.

The synthesis of the hybrid materials was carried out as follows: TiO2 was impregnated over two alkaline-activated CFA labeled HYD and CAN. Different nominal amounts of TiO2 (wt%), in the form of titanium isopropoxide, were added drop by drop to a solution of ethanol with HYD and CAN, separately, for six hours, under magnetic stirring, at 60 °C. Solutions were dried overnight at 90 °C in a muffle furnace. The hybrid materials were labeled relative to the scheme of Table 1.

The surface chemical analysis was carried out by X-ray photoelectron spectroscopy, XPS, using an X(NAP-XPS) spectrometer with a PHOIBOS 150 1D-DLD analyzer, employing an excitation source of Al-Kα (1486.7 eV, 13 kV, 100 W) with a step of 20 eV and 0.1 eV. All the spectra were calibrated with a C1s electron peak at 284.6 eV. The morphological surface features were observed by scanning electron microscopy (SEM) using a piece of LYRA3 TESCAN equipment in backscattering and secondary modes, and the chemical composition was obtained by Energy Disperse X-ray Spectroscopy (EDS).

The electrical properties were studied employing assisted laser impedance spectroscopy (ALIS) measurements in darkness and under illumination, using an unpolarized TEM 00 solid-state laser of wavelength λ = 390 nm, with a power of 35 mW/cm2. The data were collected using a homemade Bayonet Neill–Concelman connector (BNC)-based breakout box to a Keysight E4980AL-precision LCR meter. The measurements were achieved with an AC signal of 100 mV amplitude in a frequency range between 20 Hz and 1 MHz and with zero DC bias. Data were fitting using two equivalent electrical circuits using the EIS Spectrum Analyser 1.0 software31. The sample was placed in a cell of cylindrical shape comprised of two isolated stainless-steel electrodes separated by a polytetrafluoroethylene O-ring. 50 mg of the hybrid materials were diluted in 200 mL of MilliQ water; from this solution, a volume of 200 mL was used to make the measurement.

XPS spectra measurements were obtained to analyze the electronic and surface chemical states of the samples. Figure 1a,b shows the full XPS spectrum of the HYD-T-8.7 and CAN-T-8.7 samples, respectively. The spectrums show signals from Al, Si, Na, and Ti. Additionally, CAN-T-8.7 exhibits a signal originating from Fe. Al, Si, and Na arise from the zeolites and other aluminosilicates rising from alkaline-treated CFA; the Ti emerges from the impregnated TiO2 mainly, and the Fe emerges from the CFA. All hybrid materials, CAN-Ts and HYD-Ts, display similar spectrums.

Wide XPS spectra of the samples (a) HYD-T-8.7 and (b) CAN-T-8.7.

High resolution XPS spectra was performed to analyze the peaks corresponding to Ti2p (Fig. 2) and O1s (Fig. 3). These spectra were fitted with a Gaussian-peak function.

Deconvoluted spectra of the Ti2p for, (a) synthesized TiO2 (b–f) HYD-T and (g–k) CAN-T hybrid materials.

Deconvoluted spectra of the O1s for (a) synthesized TiO2 (b–f) HYD-T and (g–k) CAN-T hybrid materials.

For synthesized TiO2, two peaks at 458.5 eV and 464.4 eV emerge from spin–orbit splitting. The deconvoluted spectra for synthesized TiO2 contains main peaks at 458.5 eV, 459.7 eV, and 464.3 eV that can be assigned to Ti4+2p3/212, Ti3+2p1/213, and Ti4+2p1/232,33 respectively, Fig. 2a. The peaks corresponding to Ti4+ state is attributed to the Ti4+ of the TiO2 lattice; the peak corresponding to Ti3+ state is attributed to oxygen vacancies in the surface.

In all samples, HYD-T (Fig. 2b–f) and CAN-T (Fig. 2g–k) the peaks appear at around 458.5 eV and 464.3 eV, both corresponding to the Ti4+ state. The peak at around 459.7 eV of the Ti3+ state does not arise ; however, one third signal emerges at around 456 eV, which corresponds to the Ti3+2p3/2 state32. For CAN-T-33.25, the sample contribution of the Ti3+ state was not observed (Fig. 3i).

For synthesized TiO2, the O1s XPS high-resolution spectra contain main peaks at 529.7 eV and 530.5 eV that can be attributed to Ti–O–Ti34 and an oxygen vacancy (VO)33, respectively (Fig. 3a).

The O1s XPS spectra for both HYD-T (Fig. 3b–f) and CAN-T (Fig. 3g–k hybrid materials depict extra peaks; these were deconvoluted with peaks at 529.7 eV, 530.5 eV, 531 eV, 531.5 eV, 532.4 eV, and 534.8 eV, which can be attributed to Ti–O–Ti34, oxygen vacancy33, Ti–O12, Al–O–Al/Si–O–Al35, SiO235, and adsorbed O2/H2O34, respectively.

The relative contribution of the deconvoluted signal to the total spectra of Fig. 2. and Fig. 3. for each of the samples is provided in Fig. 4. The bars at 100 wt% of TiO2correspond to the contribution of the synthesized TiO2. The high percentage of titanium in the hybrid materials refers to a high content of TiO2on the substrate surface. For the HYD-T samples, the Ti3+ contribution decreases when the TiO2load increases until 33.25 wt% TiO2, then the Ti3+ contribution increases when TiO2load increases. Concerning the CAN-T samples, the Ti3+ contribution increases when the TiO2load increases until 25 wt% TiO2, then the Ti3+ contribution is zero for 33.25 wt% TiO2, next, the Ti3+ contribution arise for 41.3 wt% TiO2, this contribution is smaller than the contribution for 25 wt% TiO2and finally, the Ti3+ contribution decreases for 49.45 wt% TiO2. The results show that the contribution of the Ti3+ state in the TiO2phase on the surface of HYD-T samples behaves contrary to CAN-T samples as a function of the amount of loaded TiO2.

Relative contribution to the (a) O1s, (b) Ti2p peak for HYD-T; (c) O1s and (d) Ti2p peak for CAN-T hybrid materials.

Figure 5. displays the SEM images of HYD-T materials. It can be depicted that the morphology of the materials is composed of particles with two distinctive shapes, mainly. Particles are conspicuously spherically shaped in HYD-T-8.7, HYD-T-25, and HYD-T-33.25. The morphology of TiO2 changes for higher TiO2 amounts in which the particles have truncated faces in HYD-T41.3 and HYD-T49.45 samples, both shapes with smooth surfaces. These particles correspond to TiO2. It is noticed that aggregation takes place in TiO2 particles (it is evident in HYD-T-25), and it makes that particle size bigger than 2.5 mm. Particles with rod and flake shapes correspond to aluminosilicates, and the grade of aggregation is smaller than that in TiO2 particles. The aggregation of TiO2 particles indicates that the TiO2 intraparticle attachment rate is larger than the TiO2-substrate attachment rate. Elemental composition was obtained through an EDS probe. Figure 5f–k shows the EDS map for HYD-T-41.3.

SEM images of the hybrid materials HYD-T for (a) 8.7, (b) 25, (c) 33.25, (d) 41.3 and, (e) 49.45 wt% TiO2, and (f–k) EDS map of the sample HYD-T-41.3 related to the Fig. 2d.

Figure 6 displays the SEM images of CAN-T materials. It can be seen that the morphology of the materials exhibits similar behavior to that of the HYD-T samples. The spherical shape is predominant in TiO2 particles for CAN-T-25, CAN-T-33.25, CAN-T-41.3, and CAN-T-49.45; for smaller amounts of TiO2, the morphology changes to truncated faces in CAN-T-8.7. The surface of the TiO2 particles exhibits a smooth surface. The aggregation takes place in TiO2 particles, and it is larger in comparison with the aggregation of TiO2 particles in HYD-T samples. Particles with bar and flake shapes correspond to aluminosilicates. The TiO2-substrate attachment in this sample is larger in comparison with that depicted in HYD-T samples. Figure 6e–j shows the EDS map for HYD-T-25. The results show that elemental composition is due to the substrate’s aluminosilicates and TiO2, mainly with the presence of other elements, such as iron, which come from treated CFA.

SEM images of the hybrid materials HYD-T for (a) 8.7, (b) 25, (c) 33.25, (d) 41.3 and, (e) 49.45 wt % TiO2, and (f) EDS map of the sample CAN-T-25 related to the Fig. 4b.

In order to investigate the electrical behavior of the samples, ALIS response were measured in darkness and under UV light, from these measurements the Bode plots of the HYD-T and CAN-T were obtained and are shown in Figs. 7 and 8 respectively. The data reveal an increase of the impedance when the sample is illuminated with a resistive behavior at frequencies between 103 and 105 Hz, and a capacitive behavior below 103 Hz and above 105 Hz. The impedance tends to increase when the amount of TiO2 increases.

Bode plots of the samples HYD-T in dark (a) impedance, (b) phase; under illumination, (c) impedance, and (d) phase.

Bode plots of the samples CAN-T in dark (a) impedance, (b) phase; under illumination, (c) impedance, and (d) phase.

Figure 9 displays the Nyquist plots in darkness and under illumination for both series of materials, HYD-T and CAN-T. The curves exhibit two semicircles. The curvature radii of the semicircle at low frequency is larger than that at high frequency, which increases when the quantity of TiO2 increases. The curvature radii in each sample increase when radiated.

Nyquist plots of the samples HYD-T and CAN-T in darkness and under illumination.

Nyquist plots of both HYD-T and CAN-T materials in darkness and lighting conditions were fitted to an equivalent electrical circuit with resistances, capacitors and a constant phase element (CPE), shown in Fig. 10a,b. The equivalent impedances are given by Eqs. (1) and (2) for HYD-T and CAN-T materials, respectively:

where ZC = 1/jωC, ZCPE = 1/P(j(ω − ω’))α. The CPE element is explained in terms of a fractional parameter α and a parameter P = ηC, in which η is a calibration function, where R, C, P, and α are adjustable parameters. Α takes a value of + 1 or − 1 for a capacitive or inductive reactive impedance, respectively, and determines the meaning of P36.

Equivalent circuit for (a) HYD-T and (b) CAN-T hybrid materials; schematic processes in the (c) HYD-T and (d) CAN-T hybrid materials.

The adjustable parameters are reported in Tables 2 and 3 for HYD-T and CAN-T samples, respectively. Fitted parameters between light and dark conditions exhibit differences expressed as percentages, registered in Table 2. The difference was calculated according to the equation36:

It is important to elucidate the electrical conduction mechanism for TiO2@zeolite materials; however, it could be challenging to solve the exact formation mechanism. This study investigated this issue considering the following facts: (a) The distortion of the semicircles is attributed to the contribution of grain and grain boundaries. (b) A larger curvature radii in the Nyquist plots suggest a lower charge transfer at the electrolyte/electrode interface37,38,39,40,41. The radius of the semicircles increases when the TiO2 amount increases in both HYD-T and CAN-T samples, which indicates that the resistance of the entire system increases; thus, there is an increase in the charge transfer resistance crosswise the solid–liquid interface. Those resistances increase when the TiO2 amount increases and the resistance increases in each sample when the materials are illuminated. (c) The increase in the system resistance when the quantity of TiO2 increases indicates that the agglomeration of TiO2 particles (as depicted in SEM results) increases the resistance between the TiO2-substrate interface. In addition, the increases in the agglomeration of TiO2 particles increase the resistance in the TiO2. (d) The increase in the resistance of the system when illuminated indicates that the generated photoelectrons into TiO2 increase the charge concentration in the surface; it increases the capacitance contribution to the impedance of the system. Additionally, the radicals originated in the solution by oxidation processes are adsorbed by the substrate, or the generated photoelectrons on TiO2 recombine in the TiO2@zeolite solid.

According to the previous facts it is suggesting the following coherent mechanism:

For both series of samples, HYD-T and CAN-T, the value of ΔR2 is mostly positive (except for HYD-T-41.3) and it tends to increase when the TiO2 amount increases in the material, which means that resistance under illumination decreases, in comparison with resistance in darkness. This resistance is attributed to the resistance of the TiO2 because the density of electrons in the conduction band increases by the promotion of electrons from the valence band by light absorption. The value of ΔR2 is larger in the HYD-T than in the CAN-T samples, which suggests that there is a larger density of electrons on the surface of TiO2 in HYD-T than in the CAN-T samples. With this in mind, the capacitance associated with the surface of the TiO2 must increase when the material is illuminated; thus, the value of ΔC must be negative. In the CAN-T samples, ΔC2 behaves as expected; however, in HYD-T samples, the values of ΔC1 and ΔC2 are positive. These results suggest a larger electron transfer from the hybrid material to the solution in the HYD-T samples than in the CAN-T ones. Furthermore, the equivalent circuit in the HYD-T samples is two capacitors instead of the three capacitors in the CAN-T ones. Thus, the TiO2 -substrate in HYD-T fosters the charge transfer and avoids the charge accumulation in the interface TiO2 /substrate and subsequently in the interface hybrid-material/solution (see Fig. 10c). Conversely, in CAN-T samples, there is a charge accumulation in the interface TiO2 /substrate that avoids the charge transfer from the hybrid material to electrolyte and exhibits larger electron–hole recombination in the TiO2, especially in samples with wt% TiO2 larger than 25%, in which the agglomeration of TiO2 particles (SEM Figs. 5 and 6) fosters electron–hole recombination. Thus, the C2 is the capacitance in the TiO2/substrate interface in CAN-T samples. C1 is the capacitance in the electrode/solution, and R3 is the resistance in the solution; ΔC1 and ΔR3 exhibit positive values, indicating that there is a decrease of the charge accumulation in this interface and a decreasing of charge carriers in the solution due to charge transfer from TiO2 and electrolyte towards the substrate to neutralize the active sites in the zeolite phases. Thus, R1 is associated with the resistance of the substrate, and C3 is the capacitance in TiO2/substrate interface in CAN-T hybrid materials (see Fig. 10d). The decrease in the values of C2 under illumination (i. e., the decreasing of charge accumulation between sample/electrolyte and due to the charge transfer to promote oxidation and reduction reactions in the TiO2 surface to generate free radicals and ˙OH, the larger quantity of free radicals) is generated by HYD-T-8.7 and HYD-T-25. These samples exhibited the largest dye degradation among all samples30.

This work studied the surface and electrical properties of the previously synthesized TiO2@zeolite materials used to degrade methyl orange, in which the zeolite was obtained from CFA. XPS results verified that TiO2 corresponds to anatase with the presence of the Ti3+ state. The morphological characteristics studied by SEM images show that the TiO2 particles agglomerate, forming spherical particles. The electric behavior studied by ALIS measurements allows us to conclude that the resistance of the entire system increases when the amount of TiO2 increases. According to the XPS, SEM and ALIS results the electrical behavior mainly depends on the interactions between substrate- TiO2 and substrate/ TiO2-liquid rather than the presence of Ti3+ in the surface. The best TiO2-substrate attachment in the CAN-T samples increases the capacitive behavior between the substrate and TiO2 interface; however, the resistance of the entire system is smaller than in HYD-T samples. Conversely, the low degree of TiO2-substrate attachment in the HYD-T samples decreases the capacitive behavior between the substrate and TiO2-interface, allowing a higher transfer of the charges between the solid–liquid interface. From the results a coherent electrical mechanism to explain the differences in the methyl orange degradation by both HYD-T and CAN-T samples was proposed, finally, the electric behavior of the hybrid materials produced from CFA and TiO2 is a complex mechanism that requires additional studies to be completely elucidated.

All data generated or analyzed during this study are included in this published article.

Ikram, M. et al. Bacillus subtilis: As an efficient bacterial strain for the reclamation of water loaded with textile azo dye, orange II. Int. J. Mol. Sci. 23, 10637 (2022).

Article CAS PubMed PubMed Central Google Scholar

Karimi-Maleh, H. et al. Recent advances in carbon nanomaterials-based electrochemical sensors for food azo dyes detection. Food Chem. Toxicol. 164, 112961 (2022).

Article CAS PubMed Google Scholar

Guettaï, N. & Ait Amar, H. Photocatalytic oxidation of methyl orange in presence of titanium dioxide in aqueous suspension. Part I: Parametric study. Desalination 185, 427–437 (2005).

Article Google Scholar

Akpan, U. G. & Hameed, B. H. Parameters affecting the photocatalytic degradation of dyes using TiO2-based photocatalysts: A review. J. Hazard. Mater. 170, 520–529 (2009).

Article CAS PubMed Google Scholar

Daghrir, R., Drogui, P. & Robert, D. Modified TiO2 for environmental photocatalytic applications: A review. Ind. Eng. Chem. Res. 52, 3581–3599 (2013).

Article CAS Google Scholar

Ohno, T., Mitsui, T. & Matsumura, M. Photocatalytic activity of S-doped TiO2 photocatalyst under visible light. Chem. Lett. 32, 364–365 (2003).

Article CAS Google Scholar

Zhang, P., Yin, S. & Sato, T. Synthesis of high-activity TiO2 photocatalyst via environmentally friendly and novel microwave assisted hydrothermal process. Appl. Catal. B 89, 118–122 (2009).

Article CAS Google Scholar

Torres Arango, M. A., Kwakye-Ackah, D., Agarwal, S., Gupta, R. K. & Sierros, K. A. Environmentally friendly engineering and three-dimensional printing of TiO2 hierarchical mesoporous cellular architectures. ACS Sustain. Chem. Eng. 5, 10421–10429 (2017).

Article CAS Google Scholar

Anpo, M. Utilization of TiO2 photocatalysts in green chemistry. Pure Appl. Chem. 72, 1265–1270 (2000).

Article CAS Google Scholar

Chen, F. et al. Simultaneous realization of direct photodeposition and high H2-production activity of amorphous cobalt sulfide nanodot-modified rGO/TiO2 photocatalyst. Rare Met. 40, 3125–3134 (2021).

Article CAS Google Scholar

Díaz, L. et al. M/TiO2 (M = Fe Co, Ni, Cu, Zn) catalysts for photocatalytic hydrogen production under UV and visible light irradiation. Inorg. Chem. Front. 8, 3491–3500 (2021).

Article Google Scholar

Mahendran, V. & Gogate, P. R. Degradation of acid Scarlet 3R dye using oxidation strategies involving photocatalysis based on Fe doped TiO2 photocatalyst, ultrasound and hydrogen peroxide. Sep. Purif. Technol. 274, 119011 (2021).

Article CAS Google Scholar

Bootluck, W., Chittrakarn, T., Techato, K. & Khongnakorn, W. Modification of surface α-Fe2O3/TiO2 photocatalyst nanocomposite with enhanced photocatalytic activity by Ar gas plasma treatment for hydrogen evolution. J. Environ. Chem. Eng. 9, 105660 (2021).

Article CAS Google Scholar

Jha, B. & Singh, D. N. Basics of zeolites. in Fly Ash Zeolites: Innovations, Applications, and Directions (eds. Jha, B. & Singh, D. N.). 5–31. https://doi.org/10.1007/978-981-10-1404-8_2 (Springer, 2016).

Structural chemistry of microporous materials. in Chemistry of Zeolites and Related Porous Materials. 19–116. https://doi.org/10.1002/9780470822371.ch2 (Wiley, 2007).

Reháková, M., Čuvanová, S., Dzivák, M., Rimár, J. & Gavalόvá, Z. Agricultural and agrochemical uses of natural zeolite of the clinoptilolite type. Curr. Opin. Solid State Mater. Sci. 8, 397–404 (2004).

Article ADS Google Scholar

Bacakova, L., Vandrovcova, M., Kopova, I. & Jirka, I. Applications of zeolites in biotechnology and medicine—A review. Biomater. Sci. 6, 974–989 (2018).

Article CAS PubMed Google Scholar

Primo, A. & Garcia, H. Zeolites as catalysts in oil refining. Chem. Soc. Rev. 43, 7548–7561 (2014).

Article CAS PubMed Google Scholar

Belviso, C. Zeolite for potential toxic metal uptake from contaminated soil: A brief review. Processes 8, 820 (2020).

Article CAS Google Scholar

Sayehi, M., Garbarino, G., Delahay, G., Busca, G. & Tounsi, H. Synthesis of high value-added Na-P1 and Na-FAU zeolites using waste glass from fluorescent tubes and aluminum scraps. Mater. Chem. Phys. 248, 122903 (2020).

Article CAS Google Scholar

Supelano, G. I. et al. Synthesis of magnetic zeolites from recycled fly ash for adsorption of methylene blue. Fuel 263, 116800 (2020).

Article CAS Google Scholar

Pu, X., Yao, L., Yang, L., Jiang, W. & Jiang, X. Utilization of industrial waste lithium-silicon-powder for the fabrication of novel nap zeolite for aqueous Cu(II) removal. J. Clean. Prod. 265, 121822 (2020).

Article CAS Google Scholar

Abdelrahman, E. A., Abou El-Reash, Y. G., Youssef, H. M., Kotp, Y. H. & Hegazey, R. M. Utilization of rice husk and waste aluminum cans for the synthesis of some nanosized zeolite, zeolite/zeolite, and geopolymer/zeolite products for the efficient removal of Co(II), Cu(II), and Zn(II) ions from aqueous media. J. Hazard. Mater. 401, 123813 (2021).

Article CAS PubMed Google Scholar

Liu, Z. et al. Photocatalyst from one-dimensional TiO2 nanowires/synthetic zeolite composites. Mater. Exp. 4, 465–474 (2014).

Article ADS CAS Google Scholar

Amereh, E. & Afshar, S. Photodegradation of acetophenone and toluene in water by nano-TiO2 powder supported on NaX zeolite. Mater. Chem. Phys. 120, 356–360 (2010).

Article CAS Google Scholar

Chen, J., Eberlein, L. & Langford, C. H. Pathways of phenol and benzene photooxidation using TiO2 supported on a zeolite. J. Photochem. Photobiol. A 148, 183–189 (2002).

Article CAS Google Scholar

Nomura, Y., Fukahori, S. & Fujiwara, T. Thermodynamics of removing crotamiton and its transformation byproducts from water by a rotating advanced oxidation contactor with zeolite/TiO2 composite sheets. Chem. Eng. J. 380, 122479 (2020).

Article CAS Google Scholar

Badvi, K. & Javanbakht, V. Enhanced photocatalytic degradation of dye contaminants with TiO2 immobilized on ZSM-5 zeolite modified with nickel nanoparticles. J. Clean. Prod. 280, 124518 (2021).

Article CAS Google Scholar

Yang, L. et al. The influence of zeolites fly ash bead/TiO2 composite material surface morphologies on their adsorption and photocatalytic performance. Appl. Surf. Sci. 392, 687–696 (2017).

Article ADS CAS Google Scholar

Supelano García, I. et al. Physicochemical properties of Ti3+ self-doped TiO2 loaded on recycled fly-ash based zeolites for degradation of methyl orange. Condens. Matter 7, 69 (2022).

Article Google Scholar

Bondarenko, A. S. & Ragoisha, G. A. EIS Spectrum Analyser. (2005).

Zhang, Z. et al. Microwave-assisted self-doping of TiO2 photonic crystals for efficient photoelectrochemical water splitting. ACS Appl. Mater. Interfaces 6, 691–696 (2014).

Article CAS PubMed Google Scholar

Bharti, B., Kumar, S., Lee, H.-N. & Kumar, R. Formation of oxygen vacancies and Ti3+ state in TiO2 thin film and enhanced optical properties by air plasma treatment. Sci. Rep. 6, 32355 (2016).

Article ADS CAS PubMed PubMed Central Google Scholar

Cheng, D. et al. One-step reductive synthesis of Ti3+ self–doped elongated anatase TiO2 nanowires combined with reduced graphene oxide for adsorbing and degrading waste engine oil. J. Hazard. Mater. 378, 120752 (2019).

Article ADS CAS PubMed Google Scholar

El-Nahas, S., Osman, A. I., Arafat, A. S., Al-Muhtaseb, A. H. & Salman, H. M. Facile and affordable synthetic route of nano powder zeolite and its application in fast softening of water hardness. J. Water Process Eng. 33, 101104 (2020).

Article Google Scholar

Mesa, F., Paez-Sierra, B. A., Romero, A., Botero, P. & Ramírez-Clavijo, S. Assisted laser impedance spectroscopy to probe breast cancer cells. J. Phys. D Appl. Phys. 54, 075401 (2020).

Article ADS Google Scholar

Mao, C. et al. Integrating zeolite-type chalcogenide with titanium dioxide nanowires for enhanced photoelectrochemical activity. Langmuir 33, 13634–13639 (2017).

Article CAS PubMed Google Scholar

Optimization of TiO2/ZSM-5 photocatalysts: Energy band engineering by solid state diffusion method with calcination. in ScienceDirect. https://www.sciencedirect.com/science/article/pii/S2213343721005406?via%3Dihub.

Park, J.-A. et al. Ultrasonic spray pyrolysis synthesis of reduced graphene oxide/anatase TiO2 composite and its application in the photocatalytic degradation of methylene blue in water. Chemosphere 191, 738–746 (2018).

Article ADS CAS PubMed Google Scholar

Derikvandi, H. & Nezamzadeh-Ejhieh, A. Comprehensive study on enhanced photocatalytic activity of heterojunction ZnS-NiS/zeolite nanoparticles: Experimental design based on response surface methodology (RSM), impedance spectroscopy and GC-MASS studies. J. Colloid Interface Sci. 490, 652–664 (2017).

Article ADS CAS PubMed Google Scholar

Tayebi, M. et al. Reduced graphene oxide (RGO) on TiO2 for an improved photoelectrochemical (PEC) and photocatalytic activity. Sol. Energy 190, 185–194 (2019).

Article ADS CAS Google Scholar

Download references

This work was financed by the Gobernación de Boyacá (Grant No. 733 Colciencias). We acknowledge Fundación Universitaria Los Libertadores and Universidad Nacional de Colombia.

Grupo Física de Materiales, Universidad Pedagógica y Tecnológica de Colombia (UPTC), Avenida Central del Norte 39-115, 150003, Tunja, Boyacá, Colombia

G. I. Supelano & C. A. Parra Vargas

Fundación Universitaria Los Libertadores, Facultad de Ingeniería y Ciencias Básicas, Cra.16 # 63a-68, Bogotá, Colombia

F. Mesa

Grupo GIFAM, Universidad Antonio Nariño, Carrera 7 # 21-84, 150001, Tunja, Boyacá, Colombia

J. A. Mejía Gómez

Grupo de Materiales Nanoestructurados y sus Aplicaciones, Universidad Nacional de Colombia-Bogotá, Cra. 30, No. 45-03, Edificio 404 Lab. 121C, 11001, Bogotá, Colombia

A. Dussan

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

Conceptualization, writing, formal analysis, investigation G.I.S.; conceptualization, writing, formal analysis, investigation, resources F.M.; conceptualization, resources, supervision C.A.P.V., conceptualization, resources, supervision J.A.M.G; conceptualization, writing, formal analysis A.D. All authors reviewed the manuscript.

Correspondence to F. Mesa.

The authors declare no competing interests.

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

Supelano, G.I., Mesa, F., Vargas, C.A.P. et al. Assessment of surface and electrical properties of the TiO2@zeolite hybrid materials. Sci Rep 13, 3650 (2023). https://doi.org/10.1038/s41598-023-30529-8

Download citation

Received: 21 November 2022

Accepted: 24 February 2023

Published: 04 March 2023

DOI: https://doi.org/10.1038/s41598-023-30529-8

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.